TRILOY® 120

PC/PBT

Inquiry

TYPICAL DATA OF TRILOY® 120 GRADE

PROPERTY UNIT ASTM METHOD TYPICAL DATA
Physical
Specific Gravity - D792 1.20
Water Absorption (24 hours at 23℃) % D570 0.15
Melt Flow Rate (250℃, 3.8kg) g/10min D1238 8
MECHANICAL
Tensile Strength at yield kgf/㎠ D638 600
Tensile Elongation at break % D638 180
Flexural Strength at yield kgf/㎠ D790 800
Flexural Modulus kgf/㎠ D790 22,000
Izod Impact Strength, notched, 23℃ (1/8”) kgf∙㎝/㎝ D256 80
Rockwell Hardness R scale D785 110
THERMAL
HDT, 18.6 ㎏f/㎠ D648 120
Coefficient of Linear Thermal Expansion ㎜/㎜/℃ D696 8.3 x 10-5
ELECTRICAL
Volume Resistivity Ω∙㎝ D257 5E+16
Dielectric Strength kV/㎜ D149 23
Dielectric Constant - D150 3
Dissipation Factor - D150 0.009
ARC Resistance sec D495 118
OTHERS
UL-94 Flammability - (UL 94) HB
Mold Shrinkage (3mm thickness) % D955 0.7~1.2
※The figures listed in this table are typical values obtained under the standard test methods and may not be applicable for products that are under different application condition.

PROCESSING GUIDE FOR TRILOY® 120 GRADE

General processing conditions for TRILOY® 120 are shown below.
Drying prior to processing is essential to ensure desired appearance and property performance.

SPECIFICATION UNIT CONDITIONS
Drying Temperature 80~90
Drying Time hr 3~5
Moisture Content, Max % 0.02
Melt Temperature 250~270
Nozzle Temperature 255~265
Front Temperature 255~265
Middle Temperature 250~260
Rear Temperature 240~250
Mold Temperature 60~80