TRIEL® 5400

TPEE

문의하기

TYPICAL DATA OF TRIEL® 5400 GRADE

PROPERTY UNIT ASTM METHOD TYPICAL DATA
Physical
Specific Gravity - D792 1.13
Water Absorption (24 hours at 23℃) % D570 0.45
Melt Flow Rate (230도, 2.16kg) g/10min D1238 12
MECHANICAL
Tensile Strength at yield kgf/㎠ D638 100
Tensile Elongation at break % D638 >400
Flexural Strength at yield kgf/㎠ D790 37
Flexural Modulus kgf/㎠ D790 620
Izod Impact Strength, notched, 23℃ (1/8”) kgf∙㎝/㎝ D256 No Break
Hardness (Shore D) Shore D 40
THERMAL
HDT, 4.6 ㎏f/㎠ 57
Vicat softening temperature 143
ELECTRICAL
OTHERS
Mold Shrinkage % 1.8
※The figures listed in this table are typical values obtained under the standard test methods and may not be applicable for products that are under different application condition.

PROCESSING GUIDE FOR TRIEL® 5400 GRADE

General processing conditions for TRIEL® 5400 are shown below.
Drying prior to processing is essential to ensure desired appearance and property performance.

SPECIFICATION UNIT CONDITIONS
Drying Temperature 100~110
Drying Time hr 3~4
Moisture Content, Max % 0.02
Melt Temperature 190~220
Nozzle Temperature 190~220
Front Temperature 190~220
Middle Temperature 190~220
Rear Temperature 170~200
Mold Temperature 30~50
Back Pressure MPa 0.0~0.1
Screw Speed rpm 10~50
Vent Depth mm 0.02~0.08