TRILOY® 220

PC/ABS

문의하기

TYPICAL DATA OF TRILOY® 220 GRADE

PROPERTY UNIT ASTM METHOD TYPICAL DATA
Physical
Specific Gravity - D792 1.14
Water Absorption (24 hours at 23℃) % D570 0.2
Melt Flow Rate (250℃, 5kg) g/10min D1238 11
MECHANICAL
Tensile Strength at yield kgf/㎠ D638 540
Tensile Elongation at break % D638 180
Flexural Strength at yield kgf/㎠ D790 800
Flexural Modulus kgf/㎠ D790 23,000
Izod Impact Strength, notched, 23℃ (1/8”) kgf∙㎝/㎝ D256 55
Rockwell Hardness R scale D785 115
THERMAL
HDT, 18.6 ㎏f/㎠ D648 108
Coefficient of Linear Thermal Expansion ㎜/㎜/℃ D696 7.3 x 10-5
ELECTRICAL
Volume Resistivity Ω∙㎝ D257 5E+16
Dielectric Strength kV/㎜ D149 25
Dielectric Constant - D150 3
Dissipation Factor - D150 0.009
ARC Resistance sec D495 123
OTHERS
UL-94 Flammability (1.5mm thickness) - (UL 94) HB
Mold Shrinkage (3mm thickness) % D955 0.5~0.7
※The figures listed in this table are typical values obtained under the standard test methods and may not be applicable for products that are under different application condition.

PROCESSING GUIDE FOR TRILOY® 220 GRADE

General processing conditions for TRILOY® 220 are shown below.
Drying prior to processing is essential to ensure desired appearance and property performance.

SPECIFICATION UNIT CONDITIONS
Drying Temperature 90
Drying Time hr 3~4
Moisture Content, Max % 0.02
Melt Temperature 260~280
Nozzle Temperature 250~270
Front Temperature 255~275
Middle Temperature 255~275
Rear Temperature 245~265
Mold Temperature 60~90