TRAMID® 4110

PA6

Inquiry

TYPICAL DATA OF TRAMID® 4110 GRADE

PROPERTY UNIT ASTM METHOD TYPICAL DATA
Physical
Specific Gravity - D792 1.13
Water Absorption (24 hours at 23℃) % D570 1.1
Melt Flow Rate (260℃, 2.16kg) g/10min D1238 55
MECHANICAL
Tensile Strength at yield kgf/㎠ D638 800
Tensile Elongation at break % D638 40
Flexural Strength at yield kgf/㎠ D790 1,000
Flexural Modulus kgf/㎠ D790 28,000
Izod Impact Strength, notched, 23℃ (1/8”) kgf∙㎝/㎝ D256 5
THERMAL
HDT, 18.6 ㎏f/㎠ D648 60
ELECTRICAL
OTHERS
Mold Shrinkage (3mm thickness) % D955 1.4 ~ 1.8
※The figures listed in this table are typical values obtained under the standard test methods and may not be applicable for products that are under different application condition.

PROCESSING GUIDE FOR TRAMID® 4110 GRADE

General processing conditions for TRAMID® 4110 are shown below.
Drying prior to processing is essential to ensure desired appearance and property performance.

SPECIFICATION UNIT CONDITIONS
Drying Temperature 70~80
Drying Time hr 5~7
Moisture Content, Max % 0.25
Melt Temperature 270~290
Nozzle Temperature 270~300
Front Temperature 270~300
Middle Temperature 260~290
Rear Temperature 220~260
Mold Temperature 20~70
Back Pressure MPa 0.0~0.1
Screw Speed rpm 10~50
Vent Depth mm 0.02~0.08